Nanoscale membrane electrode assemblies based on porous anodic alumina for hydrogen–oxygen fuel cell
2007
In this paper, we demonstrate that nanoscale membrane electrode assemblies, functioning in a H 2/O 2 fuel cell, can be fabricated by impregnation of anodic alumina porous membranes with Nafion® and phosphotungstic acid. Porous anodic alumina is potentially a promising material for thin-film micro power sources because of its ability to be manipulated in micro-machining operations. Alumina membranes (Whatman, 50 μm thick, and pore diameters of 200 nm) impregnated with the proton conductor were characterized by means of scanning electron microscopy, X-ray diffraction, and thermal analysis. The electrochemical characterization of the membrane electrode assemblies was carried out by recording t…
Nanoporous alumina membranes filled with solid acid for thin film fuel cells at intermediate temperatures
2004
Thin film fuel cells have been fabricated by impregnation of inorganic porous membranes with inorganic proton conductor. Anodic alumina membranes (50 μm thick and pore diameter of 200 nm), filled with CsHSO4 salt have been used as protonic conductor in a hydrogen-oxygen fuel cell working between 423 and 443 K in dry atmosphere. Polarization curves at 433 K showing ohmic control with open circuit values near 0.8 V and short circuit current around 8 mA cm−2 have been obtained. Possible causes of degradation as well as alternative routes to overcome some of the problems encountered with this approach will be reported. Keywords: Solid acid, Anodic alumina membranes, Pore filling, Thin film fuel…